Tire having improved dynamic properties

ABSTRACT

Tire comprising a crown reinforcement formed of at least two working crown layers of reinforcing elements, crossed from one layer to the other making with the circumferential direction angles comprised between 10° and 45°. A first layer S of polymer compound is in contact with at least one working crown layer and in contact with the carcass reinforcement, the said first layer S of polymer compound extending axially as far as at least the axial end of the tread and the complex dynamic shear modulus G*, measured at 10% and 60° C. on the return cycle, of the first layer S of polymer compound is greater than 1.35 MPa.

RELATED APPLICATIONS

This is a U.S. National Phase Application under 35 USC 371 of International Application PCT/EP2015/061721 filed on May 27, 2015.

This application claims the priority of French application no. 1455970 filed Jun. 12, 2014, the entire content of which is hereby incorporated by reference.

FIELD OF THE INVENTION

The present invention relates to a tire having a radial carcass reinforcement, and more particularly a tire intended to equip vehicles that carry heavy loads and run at sustained speed, such as lorries, tractors, trailers or buses, for example.

BACKGROUND OF THE INVENTION

In the tires of heavy duty type, the carcass reinforcement is generally anchored on either side in the area of the bead and is surmounted radially by a crown reinforcement made up of at least two layers that are superimposed and formed of threads or cords which are parallel in each layer and crossed from one layer to the next, forming angles of between 10° and 45° with the circumferential direction. The said working layers that form the working reinforcement may furthermore be covered with at least one layer, referred to as a protective layer, formed of reinforcing elements which are advantageously metallic and extensible and referred to as elastic reinforcing elements. It may also comprise a layer of metal threads or cords having low extensibility, forming an angle of between 45° and 90° with the circumferential direction, this ply, referred to as the triangulation ply, being located radially between the carcass reinforcement and the first crown ply, referred to as the working ply, formed of parallel threads or cords lying at angles not exceeding 45° in terms of absolute value. The triangulation ply forms a triangulated reinforcement with at least the said working ply, this reinforcement having low deformation under the various stresses which it undergoes, the triangulation ply essentially serving to absorb the transverse compressive forces that act on all the reinforcing elements in the crown area of the tire.

Cords are said to be inextensible when the said cords exhibit, under a tensile force equal to 10% of the breaking force, a relative elongation at most equal to 0.2%.

Cords are said to be elastic when the said cords exhibit, under a tensile force equal to the breaking load, a relative elongation at least equal to 3% with a maximum tangent modulus of less than 150 GPa.

Circumferential reinforcing elements are reinforcing elements which form angles with the circumferential direction in the range +2.5°, −2.5° around 0°.

The circumferential direction of the tire, or longitudinal direction, is the direction that corresponds to the periphery of the tire and is defined by the direction in which the tire runs.

The transverse or axial direction of the tire is parallel to the axis of rotation of the tire.

The radial direction is a direction that intersects the axis of rotation of the tire and is perpendicular thereto.

The axis of rotation of the tire is the axis about which it turns in normal use.

A radial or meridian plane is a plane which contains the axis of rotation of the tire.

The circumferential median plane, or equatorial plane, is a plane perpendicular to the axis of rotation of the tire and which divides the tire into two halves.

The “elastic modulus” of a rubber compound is to be understood as meaning a secant extension modulus at 10% deformation and at ambient temperature.

As far as rubber compositions are concerned, modulus measurements are taken under tension in accordance with standard AFNOR-NFT-46002 of September 1988: the nominal secant modulus (or apparent stress, in MPa) at 10% elongation (normal temperature and relative humidity conditions in accordance with standard AFNOR-NFT-40101 of December 1979) is measured in second elongation (i.e. after an accommodation cycle).

Some current tires, referred to as “road” tires, are intended to run at high speed and over increasingly long journeys, as a result of the improvement in the road network and of the growth of the motorway network throughout the world. The combined conditions under which such a tire is called upon to run without any doubt makes possible an increase in the distance travelled, the wear on the tire being reduced, but on the other hand, the endurance of the tire and in particular of the crown reinforcement is detrimentally affected.

This is because there are stresses in the crown reinforcement and, more particularly, shear stresses between the crown layers, combined with a not-insignificant rise in the operating temperature at the ends of the axially shortest crown layer which have the effect of causing cracks in the rubber to appear and spread at the said ends.

In order to improve the endurance of the crown reinforcement of the type of tire under consideration, solutions relating to the structure and quality of the layers and/or the profiled elements of rubber compounds which are placed between and/or around the ends of the plies and, more particularly, the ends of the axially shortest ply have already been applied.

It is notably known practice to introduce a layer of rubber compound between the ends of the working layers in order to create an uncoupling between the said ends in order to limit shear stresses. Such decoupling layers must, however, exhibit a very good cohesion. Such layers of rubber compounds are, for example, described in Patent Application WO 2004/076204.

Patent FR 1 389 428, in order to improve the resistance to degradation of the rubber compounds situated near the crown reinforcement edges, recommends the use, in combination with a low-hysteresis tread, of a rubber profiled element covering at least the sides and the marginal edges of the crown reinforcement and made up of a low-hysteresis rubber compound.

Patent FR 2 222 232, in order to avoid separations between crown reinforcement plies, teaches the coating of the reinforcement ends in a cushion of rubber of Shore A hardness different from that of the tread surmounting the said reinforcement, and higher than the Shore A hardness of the profiled element of rubber compound placed between the edges of crown reinforcement and carcass reinforcement plies.

Tires produced in this way do effectively allow an improvement in performance notably in terms of endurance.

Moreover, it is known practice, in order to produce tires with a very wide tread or in order to confer greater load bearing capacity on tires of a given dimension, to introduce a layer of circumferential reinforcing elements. Patent application WO 99/24269 describes, for example, the presence of such a layer of circumferential reinforcing elements.

The layer of circumferential reinforcing elements is usually made up of at least one metal cord wound to form a turn of which the angle of layering with respect to the circumferential direction is less than 2.5°.

During testing, the inventors demonstrated that, when certain designs of this type of tire, whether or not they comprised a layer of circumferential reinforcing elements, were loaded heavily and frequently in a manner such as may be encountered when driving along twisty roads, the said tires could exhibit properties in terms of cornering stiffness that are such that cleavage occurs in the rubber compounds of which the crown reinforcement found between the working layers is made. Such cleavage is, of course, penalizing in terms of the endurance properties of the tire. Such cleavage is further accentuated when running with overload and at high speed, again on twisty roads.

SUMMARY OF THE INVENTION

It is an object of the invention to provide tires of which the dynamic properties, notably the cornering stiffness, are improved and thus of which the endurance properties are maintained whatever the degree of wear, notably in running conditions provoking severe cornering stresses.

This object is achieved according to one aspect of the invention directed to a tire with a radial carcass reinforcement comprising a crown reinforcement formed of at least two working crown layers of reinforcing elements, crossed from one layer to the other making with the circumferential direction angles comprised between 10° and 45°, a first layer S of polymer compound being in contact with at least one working crown layer and in contact with the carcass reinforcement, the said first layer of polymer compound extending axially as far as at least the axial end of the tread, the said tread radially capping the crown reinforcement and being connected to two beads by two side walls, the complex dynamic shear modulus G*, measured at 10% and 60° C. on the return cycle, of the said first layer S of polymer compound being greater than 1.35 MPa.

The complex dynamic shear modulus (G*) is a dynamic property of the layer of rubber compound. It is measured on a viscosity analyser (Metravib VA4000) according to Standard ASTM D 5992-96. The response of a sample of vulcanized composition (cylindrical test specimen 4 mm thick and 400 mm² in cross section), subjected to sinusoidal loading in simple alternating shear stress at a frequency of 10 Hz, at a temperature of 60° C. is recorded. The sweep is carried out in deformation amplitude from 0.1 to 50% (outward cycle), then from 50% to 1% (return cycle).

According to a preferred embodiment of the invention, the crown reinforcement of the tire comprises at least one layer of circumferential reinforcing elements.

The inventors have been able to demonstrate that choosing a first layer S having a complex shear modulus G*, measured at 10% and 60° C. on the return cycle of more than 1.35 MPa, improves the dynamic properties and notably cornering stiffness properties of the tire, notably in running conditions that are particularly penalizing in terms of cornering cleavage.

Specifically, and in a way that is entirely unexpected to a person skilled in the art, the properties of the first layer S of polymer compound, the said layer S being positioned in contact with the carcass reinforcement and with at least one layer of the crown reinforcement, have an appreciable influence on the cornering stiffness properties. The inventors have further demonstrated that the choice of this first layer S of polymer compound does not impair the performance in terms of the stresses experienced by the tire when driving in a straight line.

The inventors have also been able to demonstrate that, even in the presence of a layer of circumferential reinforcing elements which does nevertheless give significant stiffness to the tire, more particularly to the crown reinforcement thereof, the features listed hereinabove for the first layer S make a notable contribution to this cornering stiffness property.

The presence of a layer of circumferential reinforcing elements would appear to be able to influence the cornering stiffness properties sufficiently and, in theory, optimally, on account of the stiffness it confers upon the tire. Tests carried out have demonstrated that the properties of the first layer S have an appreciable effect on the cornering stiffness properties of the tire and allow these to be improved even when a layer of circumferential reinforcing elements is present.

Advantageously according to an embodiment of the invention, the complex shear modulus G*, measured at 10% and 60° C. on the return cycle, of the first layer S is less than 2 MPa, so that the thermal properties of the tire are not excessively modified in case that impairs the endurance properties of the tire and the rolling resistance properties thereof.

Advantageously also, the maximum value of tan(δ), denoted tan(δ)max, of the first layer S is less than 0.100.

According to a preferred embodiment of the invention, the first layer S of polymer compound comprises a reinforcing filler made up of:

-   a) either carbon black with a BET specific surface area of between     30 and 160 m²/g, used in a content equal to or greater than 15 phr     and less than or equal to 28 phr, -   b) or a white filler of the silica and/or alumina type comprising     SiOH and/or AlOH surface functional groups selected from the group     formed of precipitated or pyrogenated silicas, aluminas or     aluminosilicates or alternatively carbon blacks modified during or     after synthesis with a specific surface area of between 30 and 260     m²/g used at a content greater than or equal to 15 phr and less than     or equal to 55 phr, -   c) or a blend of carbon black described at (a) and a white filler     described at (b), in which the overall filler content is greater     than or equal to 15 phr and less than or equal to 50 phr and the     white filler phr content is greater than or equal to the phr content     of carbon black minus 5.

The inventors have further demonstrated that the first layer S has enough cohesion to limit the spread of cracks that begin when an object pierces the tread of the tire. The inventors also demonstrate the reaching of a tire performance compromise combining the dynamic properties, notably the cornering stiffness, the rolling resistance and the endurance properties even in the abovementioned case when an object pierces the tread of the tire.

Within the meaning of the invention, a cohesive rubber compound is a rubber compound that is notably robust in relation to cracking. The cohesion of the compound is thus evaluated by a fatigue cracking test performed on a “PS” (pure shear) test specimen. It consists in determining, once the test specimen has been notched, the crack propagation rate “PR” (nm/cycle) as a function of the energy release rate “E” (J/m²). The experimental range covered by the measurement is comprised in the range −20° C. and +150° C. in terms of temperature, in an atmosphere of air or of nitrogen. The stressing of the test specimen is an imposed dynamic movement with an amplitude of between 0.1 mm and 10 mm in the form of an impulsive stress loading (“haversine” tangent signal) with a rest time equal to the duration of the impulse; the frequency of the signal is of the order of 10 Hz on average.

The measurement comprises 3 parts:

-   -   An accommodation of the “PS” test specimen, of 1000 cycles at         27% deformation.     -   Energy characterization in order to determine the         “E”=f(deformation) law. The energy release rate “E” is equal to         W0*h0, with W0=energy supplied to the material per cycle and per         unit volume and h0=initial height of the test specimen.         Exploitation of the “force/displacement” acquisitions thus gives         the relationship between “E” and the amplitude of the stress         loading.     -   Measuring the cracking, after the notching of the “PS” test         specimen. The data collected result in the determination of the         crack propagation rate “PR” as a function of the applied stress         level “E”.

According to an advantageous embodiment of the invention, the tire comprises a second layer G of polymer compound radially between the carcass reinforcement and the radially innermost layer of reinforcing elements of the crown reinforcement of axial width at least equal to 70% of the width of the radially innermost layer of reinforcing elements of the crown reinforcement and having a complex shear modulus G*, measured at 10% and 60° C. on the return cycle, greater than 1.35 MPa.

According to a preferred embodiment of the invention, the axial width of the said second layer G is at most equal to the width of the radially innermost layer of reinforcing elements of the crown reinforcement and, for preference, at least equal to 90% of the width of the radially innermost layer of reinforcing elements of the crown reinforcement.

Preferably also according to this embodiment of the invention, the thickness, measured in the radial direction, of the said second layer G is greater than ϕ and preferably less than 3ϕ, ϕ being the diameter of the reinforcing elements of the radially innermost layer of crown reinforcement.

The inventors have also been able to demonstrate that the second layer G of polymer compound thus defined further contributes to improving the cornering stiffness properties of the tire by supplementing the first layer S of polymer compound and possibly a layer of circumferential reinforcing elements, if there is one.

Advantageously according to an embodiment of the invention, the complex shear modulus G*, measured at 10% and at 60° C. on the return cycle, of the second layer G is less than 2 MPa, such that the thermal properties of the tire are not excessively modified in case that impairs the endurance properties of the tire and the rolling resistance properties thereof.

Advantageously also, the maximum value of tan(δ), denoted tan(δ)max, of the second layer G is less than 0.100.

According to one preferred embodiment of this alternative form of the invention, the second layer G of polymer compound comprises a reinforcing filler made up of:

-   a) either carbon black with a BET specific surface area of between     30 and 160 m²/g, used in a content equal to or greater than 15 phr     and less than or equal to 28 phr, -   b) or a white filler of the silica and/or alumina type comprising     SiOH and/or AlOH surface functional groups selected from the group     formed of precipitated or pyrogenated silicas, aluminas or     aluminosilicates or alternatively carbon blacks modified during or     after synthesis with a specific surface area of between 30 and 260     m²/g used at a content greater than or equal to 15 phr and less than     or equal to 55 phr, -   c) or a blend of carbon black described at (a) and a white filler     described at (b), in which the overall filler content is greater     than or equal to 15 phr and less than or equal to 50 phr and the     white filler phr content is greater than or equal to the phr content     of carbon black minus 5.

Advantageously, the polymer compound that makes up the second layer G is identical to the polymer compound that makes up the first layer S.

According to one advantageous embodiment of the invention, the axially widest working crown layer is radially on the inside of the other working crown layers.

According to an advantageous embodiment of the invention, the layer of circumferential reinforcing elements has an axial width greater than 0.5×W.

W is the maximum axial width of the tire when the latter is mounted on its service rim and inflated to its recommended pressure.

The axial widths of the layers of reinforcing elements are measured on a cross section of a tire, the tire therefore being in an uninflated state.

According to a preferred embodiment of the invention, with at least two working crown layers having different axial widths, the difference between the axial width of the axially widest working crown layer and the axial width of the axially least-wide working crown layer is comprised between 10 and 30 mm.

According to a preferred embodiment of the invention, a layer of circumferential reinforcing elements is placed radially between two working crown layers.

According to this embodiment of the invention, the layer of circumferential reinforcing elements makes it possible to limit more significantly the extent to which the reinforcing elements of the carcass reinforcement are placed under compression than a similar layer placed radially on the outside of the working layers is able to achieve. It is preferably separated radially from the carcass reinforcement by at least one working layer so as to limit the stress loadings on the said reinforcing elements and avoid excessively fatiguing them.

Advantageously too according to an embodiment of the invention, the axial widths of the working crown layers radially adjacent to the layer of circumferential reinforcing elements are greater than the axial width of the said layer of circumferential reinforcing elements and, for preference, the said working crown layers adjacent to the layer of circumferential reinforcing elements are, on either side of the equatorial plane and in the immediate axial continuation of the layer of circumferential reinforcing elements, coupled over an axial width and then decoupled by the said layer of rubber compound at least over the remainder of the width that the said two working layers have in common.

The presence of such couplings between the working crown layers adjacent to the layer of circumferential reinforcing elements allows a reduction in the tensile stresses acting on the axially outermost circumferential elements situated closest to the coupling.

According to one advantageous embodiment of the invention, the reinforcing elements of at least one layer of circumferential reinforcing elements are metallic reinforcing elements having a secant modulus at 0.7% elongation comprised between 10 and 120 GPa and a maximum tangent modulus of less than 150 GPa.

According to a preferred embodiment, the secant modulus of the reinforcing elements of 0.7% elongation is less than 100 GPa and greater than 20 GPa, preferably comprised between 30 and 90 GPa and more preferably still, less than 80 GPa.

Also preferably, the maximum tangent modulus of the reinforcing elements is less than 130 GPa and more preferably less than 120 GPa.

The modulus values expressed hereinabove are measured on a curve of tensile stress as a function of elongation determined with a preload of 20 MPa, divided by the cross section of metal of the reinforcing element, the tensile stress corresponding to a measured tension divided by the cross section of metal of the reinforcing element.

The modulus values for the same reinforcing elements may be measured from a curve of tensile stress as a function of elongation which is determined with a preload of 10 MPa divided by the overall cross section of the reinforcing element, the tensile stress corresponding to a measured tension divided by the overall cross section of the reinforcing element. The overall cross section of the reinforcing element is the cross section of a composite element made up of metal and of rubber, the latter notably having penetrated the reinforcing element during the tire curing phase.

According to this formulation relating to the overall cross section of the reinforcing element, the reinforcing elements of the axially outer parts and of the central part of at least one layer of circumferential reinforcing elements are metallic reinforcing elements having a secant modulus of 0.7% elongation comprised between 5 and 60 GPa and a maximum tangent modulus of less than 75 GPa.

According to one preferred embodiment, the secant modulus of the reinforcing elements at 0.7% elongation is less than 50 GPa and greater than 10 GPa, preferably comprised between 15 and 45 GPa, and more preferably still, less than 40 GPa.

Also preferably, the maximum tangent modulus of the reinforcing elements is less than 65 GPa and more preferably less than 60 GPa.

According to one preferred embodiment, the reinforcing elements of at least one layer of circumferential reinforcing elements are metallic reinforcing elements having a curve of tensile stress as a function of relative elongation that has shallow gradients for small elongations and a substantially constant and steep gradient for greater elongations. Such reinforcing elements of the additional ply are normally known as “bimodulus” elements.

According to a preferred embodiment of the invention, the substantially constant and steep gradient appears upwards of a relative elongation of between 0.1% and 0.5%.

The various characteristics of the reinforcing elements mentioned above are measured on reinforcing elements taken from tires.

Reinforcing elements more particularly suited to the creation of at least one layer of circumferential reinforcing elements according to the invention are, for example, assemblies of formula 21.23, the makeup of which is 3×(0.26+6×0.23) 4.4/6.6 SS; this stranded cord being made up of 21 elementary threads of formula 3×(1+6), with 3 strands twisted together, each one made up of 7 threads, one thread forming a central core of a diameter equal to 26/100 mm, and 6 wound threads of a diameter equal to 23/100 mm Such a cord has a secant modulus of 0.7% equal to 45 GPa and a maximum tangent modulus equal to 98 GPa, these being measured on a curve of tensile stress as a function of elongation determined with a preload of 20 MPa divided by the cross section of metal of the reinforcing element, the tensile stress corresponding to a measured tension divided by the cross section of metal of the reinforcing element. On a curve of tensile stress as a function of elongation determined with a preload of 10 MPa divided by the overall cross section of the reinforcing element, the tensile stress corresponding to a measured tension divided by the overall cross section of the reinforcing element, this cord of formula 21.23 has a secant modulus of 0.7% equal to 23 GPa and a maximum tangent modulus equal to 49 GPa.

In the same way, another example of reinforcing elements is an assembly of formula 21.28, the construction of which is 3×(0.32+6×0.28) 6.2/9.3 SS. This cord has a secant modulus at 0.7% equal to 56 GPa and a maximum tangent modulus equal to 102 GPa, these measured on a curve of tensile stress as a function of elongation determined with a preload of 20 MPa divided by the cross section of metal of the reinforcing element, the tensile stress corresponding to a measured tension divided by the cross section of metal of the reinforcing element. On a curve of tensile stress as a function of elongation determined with a preload of 10 MPa divided by the overall cross section of the reinforcing element, the tensile stress corresponding to a measured tension divided by the overall cross section of the reinforcing element, this cord of formula 21.28 has a secant modulus of 0.7% equal to 27 GPa and a maximum tangent modulus equal to 49 GPa.

The use of such reinforcing elements in at least one layer of circumferential reinforcing elements notably makes it possible to maintain satisfactory stiffnesses of the layer even after the shaping and curing stages in conventional manufacturing methods.

According to a second embodiment of the invention, the circumferential reinforcing elements may be formed of metallic elements that are inextensible and cut in such a way as to form portions of a length very much less than the circumference of the least-long layer, but preferably greater than 0.1 times the said circumference, the cuts between portions being axially offset from one another. Preferably again, the tensile modulus of elasticity per unit of width of the additional layer is less than the tensile modulus of elasticity, measured under the same conditions, of the most extensible working crown layer. Such an embodiment makes it possible, in a simple way, to confer upon the layer of circumferential reinforcing elements a modulus that can easily be adjusted (by means of the choice of spacings between portions of the same row) but that is in all cases lower than the modulus of the layer made up of the same metallic elements but continuous, the modulus of the additional layer being measured on a vulcanized layer of cut elements, taken from the tire.

According to a third embodiment of the invention, the circumferential reinforcing elements are wavy metallic elements the ratio a/λ of the amplitude of the waves to the wavelength being at most equal to 0.09. Preferably, the tensile modulus of elasticity per unit width of the additional layer is less than the tensile modulus of elasticity, measured under the same conditions, of the most extensible working crown layer.

The metallic elements are preferably steel cords.

According to a preferred embodiment of the invention, the reinforcing elements of the working crown layers are inextensible metal cords.

An embodiment of the invention also advantageously, in order to reduce the tensile stresses acting on the axially outermost circumferential elements, plans for the angle formed with the circumferential direction by the reinforcing elements of the working crown layers to be less than 30° and preferably less than 25°.

According to another advantageous embodiment of the invention, the working crown layers comprise reinforcing elements which are crossed from one ply to the other, making with the circumferential direction angles that can vary in the axial direction, the said angles being greater on the axially outer edges of the layers of reinforcing elements than the angle of the said elements measured at the circumferential midplane. Such an embodiment of the invention makes it possible to increase the circumferential stiffness in certain regions while on the other hand decreasing it in others, notably in order to reduce the extent to which the carcass reinforcement is placed under compression.

One preferred embodiment of the invention also provides for the crown reinforcement to be supplemented radially on the outside by at least one additional layer, referred to as a protective layer, of reinforcing elements, referred to as elastic reinforcing elements, that are oriented with respect to the circumferential direction at an angle of between 10° and 45° and in the same direction as the angle formed by the inextensible elements of the working layer radially adjacent to it.

The protective layer may have an axial width less than the axial width of the least-wide working layer. The said protective layer can also have an axial width greater than the axial width of the narrowest working layer, such that it overlaps the edges of the narrowest working layer and, when it is the layer radially above which is narrowest, such that it is coupled, in the axial extension of the additional reinforcement, with the widest working crown layer over an axial width in order thereafter, axially on the outside, to be decoupled from the said widest working layer by profiled elements having a thickness at least equal to 2 mm. The protective layer formed of elastic reinforcing elements can, in the abovementioned case, on the one hand be optionally decoupled from the edges of the said narrowest working layer by profiled elements having a thickness substantially less than the thickness of the profiled elements separating the edges of the two working layers and, on the other hand, have an axial width less than or greater than the axial width of the widest crown layer.

According to any one of the embodiments of the invention mentioned above, the crown reinforcement may furthermore be supplemented, radially on the inside between the carcass reinforcement and the radially internal working layer closest to said carcass reinforcement, by a triangulation layer made of metal inextensible reinforcing elements that are made of steel and form, with the circumferential direction, an angle of more than 60° and in the same direction as the angle formed by the reinforcing elements of the radially closest layer of the carcass reinforcement.

The tire according to the invention as has just been described therefore has improved cornering stiffness properties and thus heightened performance in terms of endurance whatever the running conditions.

BRIEF DESCRIPTION OF THE DRAWINGS

Further details and advantageous features of the invention will become apparent hereinafter from the description of exemplary embodiments of the invention, with reference to FIGS. 1 and 2 which depict:

FIG. 1: a schematic meridian view of a tire according to a first embodiment of the invention,

FIG. 2: a schematic meridian view of a tire according to a second embodiment of the invention.

In order to make them easier to understand, the figures are not shown to scale. The figures depict only half a view of a tire which extends symmetrically with respect to the axis XX′ that represents the circumferential meridian plane, or equatorial plane, of a tire.

DETAILED DESCRIPTION OF THE DRAWINGS

In FIG. 1, the tire 1, of size 315/70 R 22.5, has an aspect ratio H/S equal to 0.70, H being the height of the tire 1 on its mounting rim and S being its maximum axial width. The said tire 1 comprises a radial carcass reinforcement 2 fixed in two beads, not shown in the figure. The carcass reinforcement is formed of a single layer of metal cords. This carcass reinforcement 2 is hooped by a crown reinforcement 4 formed radially, from the inside to the outside:

-   -   of a first working layer 41 formed of non-wrapped inextensible         9.28 metal cords, which are continuous across the entire width         of the ply, and oriented at an angle equal to 24°,     -   of a layer of circumferential reinforcing elements 42, formed of         21×23 steel metal cords, of the “bimodulus” type,     -   of a second working layer 43 formed of non-wrapped inextensible         9.28 metal cords, which are continuous across the entire width         of the ply, oriented at an angle equal to 24°, and crossed with         the metal cords of the layer 41,     -   of a protective layer 44 formed of elastic 6.35 metal cords.

The crown reinforcement is itself capped by a tread 6.

The maximum axial width of the tire is equal to 317 mm.

The axial width L₄₁ of the first working layer 41 is equal to 252 mm.

The axial width L₄₃ of the second working layer 43 is equal to 232 mm. The difference between the widths L₄₁ and L₄₃ is equal to 15 mm.

As for the axial width L₄₂ of the layer of circumferential reinforcing elements 42, this is equal to 194 mm.

The last crown ply 44, referred to as the protective ply, has a width L₄₄ equal to 124 mm.

According to the invention, a first layer S of rubber compound is placed between the carcass reinforcement 2 and the first working layer 41.

In FIG. 2, the tire 1 differs from the one depicted in FIG. 1 in that a second layer G axially extends the first layer S, radially between the carcass reinforcement 2 and the first working layer 41.

Tests have been conducted with various tires S1 and S2 produced according to the invention. The tire S2 is produced as depicted in FIG. 1, and the tire S1 does not comprise a layer of circumferential reinforcing elements. These tires according to the invention S1 and S2 are compared with a reference tire T1, not comprising a layer of circumferential reinforcing elements and of which the complex dynamic shear modulus G*, measured at 10% and 60° C. on the return cycle, of the said first layer S of polymer compound is less than 1.35 MPa.

The various compounds used for the first layer S are listed below.

Compound Compound R = 1 1 NR 100 100 Black N326 5 Black N330 35 Silica 165G 40 Antioxidant (6PPD) 0.7 1.5 Stearic acid 1.4 1 Zinc oxide 2.1 5 Silane-on-black 5 Sulphur 2.15 1.75 PEG 2.5 Accelerator CBS 1 0.9 Coaccelerator DPG 0.34 Retarder CTP PVI) 0.08 MA₁₀ (MPa) 3.4 4.3 tan(δ)_(max) 0.074 0.087 P60 (%) 11.3 16.5 G* 10% at 60° C. 1.25 1.55 (return cycle)

The values for the constituent ingredients are expressed in phr (parts by weight per hundred parts of elastomer).

The reference tire T1 has a first layer S made of the compound R1.

The tires according to the invention S1 and S2 has a first layer S made of the compound 1.

First endurance tests were run on a test machine that forced each of the tires to run in a straight line at a speed equal to the maximum speed rating prescribed for the said tire (the speed index) under an initial load of 4000 kg progressively increased in order to reduce the duration of the test.

It was found that all the tires tested exhibited substantially comparable results.

Other endurance tests were conducted on a test machine that cyclically imposed a transverse loading and a dynamic overload on the tires. The tests were carried out for the tires according to the invention under conditions identical to those applied to the reference tires.

The distances covered varied from one type of tire to another, failures occurring as a result of degradation of the rubber compounds at the ends of the working layers. The results are set out in the table which follows with reference to a base 100 fixed for the reference tire T1.

Tire T1 Tire S1 Tire S2 100 125 135

These results show that the first layer S according to the invention, of which the complex dynamic s hear modulus G*, measured at 10% and 60° C. on the return cycle, is greater than 1.35 MPa, allows a very significant improvement in the endurance performance and, more particularly, the cornering stiffness properties of the tire, even when a layer of circumferential reinforcing elements is present.

The scope of protection of the invention is not limited to the examples given hereinabove. The invention is embodied in each novel characteristic and each combination of characteristics, which includes every combination of any features which are stated in the claims, even if this feature or combination of features is not explicitly stated in the examples. 

The invention claimed is:
 1. Tire with a radial carcass reinforcement comprising a crown reinforcement formed of at least two working crown layers of reinforcing elements, crossed from one layer to the other making with the circumferential direction angles comprised between 10° and 45°, a first layer of polymer compound being in contact with at least one working crown layer and in contact with the carcass reinforcement, said first layer of polymer compound extending axially as far as at least the axial end of the tread, said tread radially capping the crown reinforcement and being connected to two beads by two sidewalls, wherein the complex dynamic shear modulus, measured at 10% and 60° C. on the return cycle, of said first layer of polymer compound is greater than 1.35 MPa, wherein the maximum value of tan(δ), denoted tan(δ)max, of the first layer of polymer compound is less than 0.100, the tire further comprises a second layer of polymer compound axially in contact with the first layer of polymer compound radially between the carcass reinforcement and the radially innermost layer of reinforcing elements of the crown reinforcement, and wherein the complex dynamic shear modulus, measured at 10% and 60° C. on the return cycle, of said second layer of polymer compound is greater than 1.35 MPa.
 2. The tire according to claim 1, wherein the crown reinforcement comprises at least one layer of circumferential reinforcing elements.
 3. The tire according to claim 2, wherein the layer of circumferential reinforcing elements is placed radially between two working crown layers.
 4. The tire according to claim 3, wherein the axial widths of the working crown layers radially adjacent to the layer of circumferential reinforcing elements are greater than the axial width of the said layer of circumferential reinforcing elements.
 5. The tire according to claim 4, wherein the working crown layers radially adjacent to the layer of circumferential reinforcing elements are, on each side of the equatorial plane and in the immediate axial continuation of the layer of circumferential reinforcing elements, coupled over an axial width and then decoupled by profiled elements made of rubber compound at least over the remainder of the width that said two working layers have in common.
 6. The tire according to claim 2, wherein the reinforcing elements of at least one layer of circumferential reinforcing elements are metallic reinforcing elements having a secant modulus at 0.7% elongation comprised between 10 and 120 GPa and a maximum tangent modulus less than 150 GPa.
 7. The tire according to claim 1, wherein the complex shear modulus, measured at 10% and 60° C. on the return cycle, of the first layer of polymer compound is less than 2 MPa.
 8. The tire according to claim 1, wherein said first layer of polymer compound comprises a reinforcing filler composed of: a) either carbon black with a BET specific surface area of between 30 and 160 m2/g, used in a content equal to or greater than 15 phr and less than or equal to 28 phr, b) or a white filler of the silica and/or alumina type comprising SiOH and/or AlOH surface functional groups selected from the group formed of precipitated or pyrogenated silicas, aluminas or aluminosilicates or alternatively carbon blacks modified during or after synthesis with a specific surface area of between 30 and 260 m2/g used at a content greater than or equal to 15 phr and less than or equal to 55 phr, c) or a blend of carbon black described at (a) and a white filler described at (b), in which the overall filler content is greater than or equal to 15 phr and less than or equal to 50 phr and the white filler phr content is greater than or equal to the phr content of carbon black minus
 5. 9. The tire according to claim 1, wherein the complex shear modulus, measured at 10% and 60° C. on the return cycle, of the second layer of polymer compound is less than 2 MPa.
 10. The tire according to claim 1, wherein the maximum value of tan(δ), denoted tan(δ)max, of the second layer of polymer compound is less than 0.100.
 11. The tire according to claim 1, wherein said second layer of polymer compound comprises a reinforcing filler made up of: a) either carbon black with a BET specific surface area of between 30 and 160 m2/g, used in a content equal to or greater than 15 phr and less than or equal to 28 phr, b) or a white filler of the silica and/or alumina type comprising SiOH and/or AlOH surface functional groups selected from the group formed of precipitated or pyrogenated silicas, aluminas or aluminosilicates or alternatively carbon blacks modified during or after synthesis with a specific surface area of between 30 and 260 m2/g used at a content greater than or equal to 15 phr and less than or equal to 55 phr, c) or a blend of carbon black described at (a) and a white filler described at (b), in which the overall filler content is greater than or equal to 15 phr and less than or equal to 50 phr and the white filler phr content is greater than or equal to the phr content of carbon black minus
 5. 12. The tire according to claim 1, wherein the reinforcing elements of the working crown layers are inextensible.
 13. The tire according to claim 1, wherein the crown reinforcement is supplemented radially on the outside by at least one additional ply, referred to as a protective ply, of reinforcing elements referred to as elastic elements, which are oriented with respect to the circumferential direction at an angle of between 10° and 45° in the same direction as the angle formed by the inextensible elements of the working ply radially adjacent to it.
 14. The tire according to claim 1, wherein the crown reinforcement further comprises a triangulation layer formed of metallic reinforcing elements making angles greater than 60° with the circumferential direction. 